My point was that x isn't always better than y. And in the case of turbine blades, monocrystalline is the way they are made.
On the topic of forged turbine blades, the oriented strength of the resultant blade _is_ the advantage of using forging over conventional casting for a polycrystalline blade. Since the load on a turbine blade is mostly axial it makes no sense to not have favorable grain orientation to maximize strength in the axial direction. As a result, turbine blades are forged such that the grain orientation and size is elongated and coarse. This minimizes grain boundary area perpendicular to the load direction and thus minimizes creep at the high operating temperatures of a gas turbine.
Thanks for the insight! My original message was just me not understanding your real point. I'm usually little allergic to an attitude like "you can't understand this high magic!", but in this case I must apologize my misunderstanding.
On the topic of forged turbine blades, the oriented strength of the resultant blade _is_ the advantage of using forging over conventional casting for a polycrystalline blade. Since the load on a turbine blade is mostly axial it makes no sense to not have favorable grain orientation to maximize strength in the axial direction. As a result, turbine blades are forged such that the grain orientation and size is elongated and coarse. This minimizes grain boundary area perpendicular to the load direction and thus minimizes creep at the high operating temperatures of a gas turbine.